CEMENT ALL Plus Multi-Repair Mortar

Application

CEMENT ALL Plus is a multifunctional, plastic-modified quick-repair mortar suitable for concrete repair, grouting work, anchoring and grouting work, filling, formwork work and road repairs. Can be used indoors and outdoors, even in wet areas.

Sustainable construction

The use of CEMENT ALL Plus reduces the CO2 footprint, increases energy and resource efficiency and conserves natural resources. The production of Rapid Set cement requires 30% less CO2 emissions than conventional Portland cement. For further information (e.g. LEED values), please contact the responsible KORODUR contact person.

Properties

• multifunctional for
• repair and new construction
• horizontally and vertically
• Installation thickness "0" - 100 mm
• Faster hardening, loadable after approx. 1 hour after the end of solidification
• High-strength
• Permanently
• stress-free
• plastic-modified Increased
• carbonation resistance
• Improved frost / de-icing salt resistance due to plastic modification
• sulfate-resistant
• chloride-free
• resistant to many chemical attacks
• excellent adhesion: direct, without adhesive bridge
• post-treatment only with water
• inside and outside
• high storage stability

• substrate: clean the substrate, remove loose components, cement sludge, dust, acids, oil and grease. For a force-fit composite, the surface must be crack-free, even, rough and open-pored. The surface tensile strengths required by the regulations must be observed (1 N/mm² must not be less than 1 N/mm²). Before processing, the substrate must be thoroughly pre-wetted. In the case of highly absorbent surfaces, pre-wetting may have to be repeated several times*. A film of water or puddles should be avoided. * If necessary, an acrylate-based primer must be integrated.

• Processing: Sufficient personnel and suitable equipment or tools should be available before the work begins. Mix CEMENT ALL Plus with the specified amount of water for approx. 1 - 3 minutes in a suitable compulsory mixer or agitator, depending on the type of processing. To mix, first add water to the mixing container. Then add CEMENT ALL Plus while the mixer or stirring whisk is running. If less water is added, the strengths increase, whereby the maximum water addition must NOT be exceeded. CEMENT ALL Plus can be processed using conventional methods. Finishing should be done as soon as possible. CEMENT ALL Plus can be smoothed, rubbed or textured. The installation should be carried out in a compl. layer, i.e. not layer by layer and as evenly as possible. No installation on frozen surfaces. During compaction, air voids should be prevented as far as possible. At temperatures > 20 °C, the processing time is shortened, at temperatures < 20 °C, the development of strength can be delayed. To extend the processing time, Rapid Set SET CONTROL (retardant) or Rapid Set FLOW CONTROL (plasticizer) for increased flowability, as well as the additive FAST to accelerate the setting time, can be added (see CONCRETE PHARMACY data sheet).

After-treatment

with water must be carried out immediately as soon as the surface has lost its damp shine and should be carried out repeatedly within one hour until the product has reached sufficient strength. If longer setting times occur, temperatures are too low or a retardant is used, longer follow-up treatment times may be necessary.

Delivery form

25 kg paper special packaging

Storage

Store in a dry place like cement. Shelf life approx. 12 months.

Quality: C55/67

Grain size: 0 - 1 mm

Colour: light grey

Common installation thicknesses (*in the 1st step depending on the selected consistency):

• Floor: 10 - 100 mm
• Ceiling / overhead: 5 - 10 mm*
• Wall: 5 - 15 mm*

Setting time (based on DIN EN 196-3):

• Start of solidification: approx. 15 minutes
• End of solidification: approx. 35 minutes

Load-bearing capacity: after approx. 60 minutes

ofreadiness for paving (Readiness for paving is independent of the layer thickness and is influenced by the ambient temperature and humidity. It is recommended to check the residual moisture by means of a suitable measurement.):

• Diffusion-open coverings (e.g. tiles, diffusion-open paints): after approx. 2 hours
• Diffusion-tight coverings (e.g. parquet, bitumen waterproofing): after approx. 16 hours

Compressive strength [N/mm2] (DIN EN 1015-11):

• after 60 minutes: > 20.0 N/mm2
• after 180 minutes: > 31.0 N/mm2
• after 7 days: > 41.0 N/mm2
• after 28 days: > 62.0 N/mm2

Flexural tensile strength [N/mm2] (DIN EN 1015-11):

• after 60 minutes: > 6.0 N/mm2
• after 180 minutes: > 8.0 N/mm2
• after 28 days: > 11.0 N/mm2

Tensile adhesion strength [N/mm2] (DIN EN 1542):

• i. M. approx. 2.1 N/mm2, requirement fulfilled: yes

Static modulus of elasticity [N/mm2] (DIN EN 13412):

• approx. 31,700 N/mm2, requirement fulfilled: yes

Sulphate resistance (test according to Wittekindt):

• requirement fulfilled: yes

Penetration test (penetration of water-polluting substances acc. DAfStb Directive):

• Penetration depth i. m. 16.0 mm, requirements met: yes

Frost / de-icing salt test (CDF) (BWA leaflet frost test):

• Requirements met: yes

Chloride ion content (DIN EN 1015-17):

• i. M. 0.009, Requirements met: yes

Temperature (processing, ambient and substrate temperature): ≥ 5 °C

Water addition:

• per 25 kg container: approx. 4.0 l

Material consumption:

• per m2 per mm: approx. 2.0 kg